Fiberglass Biaxial Fabric ( 0 °- 90° )
Fiberglass Biaxial Fabric – ( 0°/ 90°)
Fiberglass stitch bonded fabric is made of fiberglass direct roving parallel aligned in 0°and 90°directions, then stitched together with chopped strand layer or polyester tissue layer as combo mat. It is compatible with Polyester, Vinyl and Epoxy resin and widely used in boat building, wind energy, automotive, sports equipment, flat panels etc, suitable Vacuum infusion, hand lay-up, pultrusion, RTM forming processes.
General Data
| Code | Weight (g/m2) | Warp (g/m2) | Weft (g/m2) | Chop layer (g/m2) | Polyester tissue layer (g/m2) | Moisture content | Wet speed (≤S) |
| ELT400 | 400 | 224 | 176 | - | - | ≤0.2 | ≤60 |
| ELT400/45 | 445 | 224 | 176 | - | 45 | ≤0.2 | ≤60 |
| ELTM400/200 | 600 | 224 | 176 | 200 | - | ≤0.2 | ≤60 |
| ELTM450/200 | 650 | 224 | 226 | 200 | - | ≤0.2 | ≤60 |
| ELT600 | 600 | 336 | 264 | - | - | ≤0.2 | ≤60 |
| ELTN600/45 | 645 | 336 | 264 | - | 45 | ≤0.2 | ≤60 |
| ELTM600/300 | 900 | 336 | 264 | 300 | - | ≤0.2 | ≤60 |
| ELTM600/450 | 1050 | 336 | 264 | 450 | - | ≤0.2 | ≤60 |
| ELT800 | 800 | 420 | 380 | - | - | ≤0.2 | ≤60 |
| ELTN800/45 | 845 | 420 | 380 | - | 45 | ≤0.2 | ≤60 |
| ELTM800/250 | 1050 | 420 | 380 | 250 | - | ≤0.2 | ≤60 |
| ELTM800/300 | 1100 | 420 | 380 | 300 | - | ≤0.2 | ≤60 |
| ELTM800/450 | 1250 | 420 | 380 | 450 | - | ≤0.2 | ≤60 |
| ELT1000 | 1000 | 560 | 440 | - | - | ≤0.2 | ≤60 |
| ELT1200 | 1200 | 672 | 528 | - | - | ≤0.2 | ≤60 |
| ELTM1200/300 | 1500 | 672 | 528 | 300 | - | ≤0.2 | ≤60 |
Remarks:
Roll width: Standard width in 1200mm, 1270mm, and other sizes depends on customer’s real needs, available in 200mm to 2600mm.
Packing: Fiberglass stitch bonded fabric usually rolled on a paper tube with inner diameter 76mm. The roll is warped with plastic film, then put into carton. Lay the rolls horizontally, and can be loaded on pallets and bulk in container.
Storage: The product should be stored in a cool, water-proof area. It is recommended that the room temperature and humidity be always maintained at 15℃ to 35℃ and 35% to 65% respectively. Please keep the product in its original packaging before being used, avoiding moisture absorption.